Polycore Tubing

 

  • Extremely high corrosion resistance and wear resistance in the HDPE liner tubing which is an excellent solution for controlling oil well corrosion and partial wear. 
  • Five times of wear resistance compare HDPE to carbon steel. 
  • Extended 4 to 7 times repair free time of oil well, and the operation cost has been greatly reduced

HDPE Liner Tubing/ Polycore Tubing  

In 2003, Shengji as the first Chinese company who introduce HDPE liner tubing production line. Up to now, SJ has produced 15 million meters HDPE liner tubing for more than 10,000 wells in China and abroad. Extended 4 to 7 times repair free time of oil well, and greatly reduced operation cost. Products are exported to Oman, Bahrain, Ecuador, Algeria, Kazakhstan, Turkmenistan, Sudan,etc.  

Product Features 

1.Advanced: It is the most effective anti-wear technology in the world; 

2.Wear resistance: low friction coefficient, wear resistance is more than five times of carbon steel; 

3.Anti-corrosion: resistant to all kinds of acid, alkali, salt; 

4.Anti-scaling: the inner wall is smooth and the polarity is strong; 

5.Adaptability: Oil and water wells are easy to operate and adapt to changes in temperature and load; 

Technical Parameter

S/N Indicator Type Technical Indicators and Test Conditions Technical Requirement Test Standard
1 Normal Temperature Properties Density,g/cm3 0.94-0.97 GB/T 1033.1
2 Shore Hardness,HD ≥65 GB/T 2411
3 Vicat Softening Temperature(A50),℃ ≥130 GB/T 1633
4 Notched Charpy Impact Strength,KJ/m2 ≥50 GB/T 1043.1
5 Elongation at Break,% ≥400 GB/T 8804.3
6 Tensile Fracture Yield Strength,MPa ≥20 GB/T 8804.3
7 Sliding Wear,mm2/m 73 ≤0.0055 Q/SH 1020 1889
8 89 ≤0.0035
9 Aging Properties Change Rate of Elongation at Break,% Oil bath at 95℃, 6d,room temperature adjustment for 48h ≤15 Q/SH 1020 1889
10 Change Rate of Tensile Fracture Yield Strength,% ≤15 Q/SH 1020 1889
11 Mortar Wear,mm ≤0.05 Q/SH 1020 1889

 

Parameter Changes compared with normal tubing

1.Change in weight

After lined, the weight increase by 7%~8%;The density of liner is 0.94g/cm3, close to oil liquid.

2.Change in ID

The inner diameter of HDPE liner tubing changes compared with normal tubing, and the specific size is as follows

Size Unlined ID Go Gauge Lined ID Go Gauge
2 7/8 62 59.62 54 51
3 1/2 76 72.82 67 64
4 1/2 100.54 97.36 89 86
  1. 3. Change in Coupling length

The purpose of using the extra long coupling is to eliminate the risk of pin ends contact and ensure that J-area gap is maintained according to API 5CT.

  1. 4. Change in working temperature

Working temperature is 100 °C, which is much lower than that of the normal tubing.

 

Product Application

Oil and water wells with well depth not exceeding 1800 m and temperature not exceeding 100 ℃.

Polycore Tubing manufacturer

HDPE Liner Tubing manufacturer

Feature Products

  • What Our Client Say About Sanjack Petro?

  • Be An Expert When Importing OCTG Tubing & Casing

    Check All Guides

    OCTG TUBING AND CASING
    OCTG Tubing Guide
    • Specifications and Grade of steel
    • PSL1 or PSL2
    • Corrosion and wear conditions
    Steel tubing pipe
    Steel Tubing Pipe Guide
    • Specifications and Grade of steel.
    • PSL1 or PSL2
    • Corrosion and wear conditions.
    VACUUM INSULATED TUBING CHINA
    Vacuum insulated tubing Guide
    • Specifications and Grade of steel.
    • The connection type.
    • Working temperature.
    TUNGSTEN COATED TUBING
    Tungsten Coated Tubing Guide
    • Corrosive composition
    • Abrasion condition
    • Working temperature.